for iron, copper and nickel materials
Castolin 1655
Cadmium-free silver solder, insensitive to overheating. Good wetting and capillary properties. For high-strength solder joints that are not susceptible to cracking. Operating temperatures from approx. -200 °C to 200 °C.
Technical data
Brazing alloy ISO 17672: ~ Ag 134
EN 1044: ~ AG 106
DIN 8513: ~ L-Ag34Sn
Flux content* EN 1045: FH 10
DIN 8513: F-SH1
Melting interval (Sol./Liq.) [°C]: 630 - 730
Working temperature [°C]: 710
Density [g/cm3]: 9.0
* if flux-coated/containing flux
Applications
For gap brazing, also in series production, e.g: Unalloyed and low-alloy steels (structural steels, case-hardening, heat-treatable and nitriding steels), high-alloy steels (stainless CrNi steels), nickel, nickel alloys,
copper and copper alloys as well as malleable cast iron (GTW).
Typical application examples are
Equipment and machinery in the food and beverage industry such as bronze and brass fittings, piping, nozzles, cladding and instruments; apparatus for heating and cooling technology.
For brazing gas installations made of copper pipes in accordance with DVGW worksheet GW 2.
Processing instructions
Clean soldering areas. Round off edges. Coat soldering surfaces with flux. Heat the tip of the soldering rod and dip it into the flux. Preheat the workpiece widely and continuously. Do not overheat. Remove corrosive flux residues.
Heat sources: Flame soldering (acetylene), flame soldering (propane/butane), HF induction, oven (with and without shielding gas), resistance heating.