1020 F Cadmium-free silver solder Ø 1.5mm/2.5kg

1020 F

Cadmium-free silver solder with low soldering temperature. Excellent wetting and capillary properties. High corrosion resistance. For tough joints with high strength. Similar in color to stainless steels. Operating temperatures from approx. - 200 °C to 200 °C.

Technical data
Brazing alloy
ISO 17672: ~ Ag 156
EN 1044: ~ AG 102
DIN 8513: ~ L-Ag55Sn

Flux content
EN 1045: FH 10
DIN 8511: F-SH1

Melting interval: 620 - 660 °C (Sol./Liq.)
Soldering temperature: 650 °C
Density: 9.4 g/cm³

Applications
For gap brazing, also in series production, e.g: Unalloyed and low-alloy steels (structural steels, case-hardening, heat-treatable and nitriding steels), high-alloy steels (stainless CrNi steels), nickel, nickel alloys, copper and copper alloys as well as malleable cast iron (GTW) and hard metals.

Typical applications are
Containers, apparatus, fittings, piping as well as equipment and machinery in the food industry such as dairies and breweries; surgical and optical instruments in medical technology; apparatus for heating and cooling technology.

Processing instructions
Clean soldering areas. Round off edges. Coat soldering surfaces with flux. Heat the tip of the soldering rod and dip it into the flux. Preheat the workpiece widely and continuously. Do not overheat. Remove any corrosive flux residue.
Heat sources: Flame soldering (acetylene; neutral to reducing)

Delivery form
1020 F: flux-coated solder rod
1020 F - Ø 1.5 x 500mm - 84 pcs/kg
1020 F - Ø 2.0 x 500mm - 49 pcs/kg