CastoWig 45612 W TIG welding rod Ø 2.4mm / 5.0kg

CastoWig 45612 W

The Ni-based weld metal is scale-resistant up to 1000 °C, heat-resistant up to 900 °C and cold-tough down to -269 °C. Not susceptible to cracking. Corrosion-resistant against media, e.g: Chlorine (dry), chlorides, fatty acids, phosphoric acid, salicylic acid and caustic soda.

Technical data
EN ISO 18274: SNi 6082
(NiCr 20 Mn 3 Nb)
AWS A5.14: ERNiCr-3
SFA 5.14: ERNiCr-3
Material no.: 2.4806

Applications
For alloy-like joint welding of
2.4816 - NiCr 15 Fe
also suitable for:
2.4851 - NiCr 23 Fe
2.4869 - NiCr 80-20
2.4669 - NiCr 15 Fe 7Ti 2Al
2.4951 - NiCr 20 Ti
2.4952 - NiCr 20Ti Al
as well as for mixed joints between high-alloy steels, e.g:
1.4539 - X 2 NiCrMoCu 25-20-5,
1.4583 - X 10 CrNiMoNb 18-12,
1.4961 - X 8 CrNiNb 16-13,
1.4981 - X 8 CrNiMoNb 16-16,
1.4988 - X 8 CrNiMoVNb 16-13
and unalloyed and low-alloyed as well as cold-tough steels, e.g:
1.0345 - P 235 GH, 1.0425 - P 265 GH,
1.0461 - S 255 N, 1.0481 - P 295 GH,
1.0562 - P 355 N, 1.4922 - X 20 CrMoV 11-1,
1.5415 - 16 Mo 3, 1.5637 - 12 Ni 14,
1.5662 - X 8 Ni 9, 1.5680 - X 12 Ni 5,
1.6311 - 20 MnMoNi 4-5, 1.6368 - 15 NiCuMoNb 5-6-4,
1.7335 - 13 CrMo 4-5, 1.7380 - 10 CrMo 9-10.
Particularly suitable for black/white connections with operating temperatures above 300 °C. Maximum permissible operating temperature +550 °C. Also for multi-layer coatings on low-alloy steels.

Processing instructions
Remove cracked and otherwise damaged material. Clean welding areas. Adjust heat conduction during welding to the component, its material and dimensions. Limit the interpass temperature to 150 °C. Ensure a continuous supply of filler material.
Form sufficiently for root welds. Use wire brushes made of austenitic CrNi steels.

Welding positions: PA, PB, PC, PE, PF
Type of current: = (-)
Shielding gas: EN ISO 14175 - I1 (100 % Ar)

Approvals
TÜV, CE