for welding steels
Properties
- High Metal Recovery: 170%
- Tensile Strength (Rm): 800 MPa
- Yield Strength (Rp0.2): 670 MPa
- Elongation (A5): 17.5%
- Hardness (after welding): 260 HV30
- Hardness (after work-hardening): 350 HV30
Description
- Application: Designed for high-speed welding of difficult-to-weld, galvanized, or dissimilar steels. Suitable for rebuilding and buttering layers before wear facing.
- Performance: High efficiency alloyed electrode with high tensile strength and crack resistance. Suitable for galvanized steels where zinc fumes are minimized while preserving the anti-corrosion properties of the zinc layer.
- Weld Yield: 170%
- Deposition Rate: High
- Weld Surface Finish: Remarkable with very easy slag removal.
Applications
- Primary Applications:
- Maximum safety margin repairs of cracks in castings, machine housings, frames, chassis, springs, etc.
- Joining dissimilar or unknown grades of steel.
- Secondary Applications:
- Machinable build-up and overlays to resist wear by friction, impact, or pressure on gears, shafts, bearings, etc.
- Cushion layer for E+C TeroCote alloys.
Technical Data
PropertyTypical Value
Yield strength R_p0.2 (N/mm²) | 674
Tensile strength R_m (N/mm²) | 803
Elongation (l=5d) (A%) | 17
Hardness (after welding) (HV30) | 260
Hardness (after work-hardening) (HV30) | 350
Welding Parameters
Diameter (mm) | Amperage (A)
1.6 | 45-60
2.0 | 75-90
2.5 | 90-120
3.2 | 120-170
4.0 | 150-240
Welding Positions
- PA, PB, PC according to ISO 06947
Packaging and Storage
- Store electrodes in a dry location to avoid humidity pick-up or coating damage.
- Re-drying conditions before use: 350°C / 2 hr if electrodes become damp.
Specification
| Code | 100127 |
|---|---|
| Category | Special alloy |
| Number in package | 5.0 kg |
| Price per unit | 143,056 £ / kg |
| Price excl. VAT | 715,28 £ |
| Price incl. VAT 20% | 858,34 £ |
| Availability | within 7 to 10 days |
Diameter: